DSpace Coleção:https://repository.ufrpe.br/handle/123456789/29142026-04-09T09:06:50Z2026-04-09T09:06:50ZESTUDO COMPARATIVO DAS PROPRIEDADES TÉRMICAS, MORFOLÓGICAS E MECÂNICAS DE PA E PLA NA IMPRESSÃO 3DSilva, Rafael Aldreem Alves dahttps://repository.ufrpe.br/handle/123456789/67462025-02-17T12:43:40Z2024-11-30T00:00:00ZTítulo: ESTUDO COMPARATIVO DAS PROPRIEDADES TÉRMICAS, MORFOLÓGICAS E MECÂNICAS DE PA E PLA NA IMPRESSÃO 3D
Autor: Silva, Rafael Aldreem Alves da
Abstract: This study conducted a comprehensive characterization of the thermal, morphological, and
mechanical properties of poly(lactic acid) (PLA) and polyamide (PA) filaments used in 3D
printing, including their carbon fiber (CF) and glass fiber (GF) reinforced variants, as well as
specialized versions for high-strength (PRO) and high-temperature (PAHT) applications. Using
Differential Scanning Calorimetry (DSC), tensile tests, and Scanning Electron Microscopy
(SEM), the thermal behavior, mechanical strength, and internal morphology of the filaments
were investigated. The results indicate that PAHT CF15, reinforced with 15% carbon fiber,
exhibits the best thermal and mechanical resistance, making it suitable for high-temperature
applications. PA6 GF30, with 30% glass fiber, offers a good balance between stiffness and
strength. In contrast, PLA White and PLA Pro materials are more suited for moderate-
temperature applications. The analysis of different infill patterns (40% and 100%) reveals that
the choice of configuration depends on cost-effectiveness, considering the specific application and desired strength. The study suggests that improvements in matrix-fiber adhesion could
optimize the performance of the composites, particularly for PAHT CF15.
Resumo: Este estudo realizou uma caracterização abrangente das propriedades térmicas, morfológicas e
mecânicas de filamentos de poli(ácido lático) (PLA) e poliamida (PA) utilizados em impressão
3D, incluindo suas variantes reforçadas com fibras de carbono (CF) e vidro (GF), bem como
versões especializadas para aplicações de alta resistência (PRO) e temperatura (PAHT). Através
de técnicas de Calorimetria Diferencial de Varredura (DSC), ensaios de tração e Microscopia
Eletrônica de Varredura (MEV), investigou-se o comportamento térmico, a resistência
mecânica e a morfologia interna dos filamentos. Os resultados indicam que o PAHT CF15,
reforçado com 15% de fibra de carbono, apresenta a melhor resistência térmica e mecânica,
sendo adequado para aplicações de alta temperatura. O PA6 GF30, com 30% de fibra de vidro,
oferece um bom equilíbrio entre rigidez e resistência. Em contrapartida, os materiais PLA
White e PLA Pro são mais indicados para aplicações em temperaturas moderadas. A análise
dos diferentes padrões de preenchimento (40% e 100%) revela que a escolha da configuração
depende do custo-benefício, considerando a aplicação específica e a resistência desejada. O
estudo sugere que melhorias na adesão matriz-fibra podem otimizar o desempenho dos
compósitos, especialmente para o PAHT CF15.2024-11-30T00:00:00ZPROTÓTIPO PARA REAPROVEITAMENTO DA ÁGUA REJEITADA NO PROCESSO DE DESTILAÇÃOLopes, Vinicius Bernard Ramoshttps://repository.ufrpe.br/handle/123456789/67422025-02-13T11:05:03Z2025-01-30T00:00:00ZTítulo: PROTÓTIPO PARA REAPROVEITAMENTO DA ÁGUA REJEITADA NO PROCESSO DE DESTILAÇÃO
Autor: Lopes, Vinicius Bernard Ramos
Abstract: Water is an indispensable natural resource for life on planet Earth. It holds immense
environmental, social, and economic value, fundamental to the survival of humans and
ecosystems on our planet. Proper water resource management should consider reuse as an
integral component, as it not only generates savings but also helps prevent water scarcity. In
Brazil, water is primarily used for crop irrigation, public supply, industrial activities, energy
generation, mineral extraction, aquaculture, navigation, tourism, and recreation. This study addresses the issue of water waste during the distillation process and is dedicated to
developing a system to reuse the rejected water generated during the process, aiming to
generate savings and reduce waste. Comparing the two production methods, we can observe
that while the usual production method uses approximately 8,580 liters (distilled + waste) of
water over 12 months, the proposed production method in this study uses only 627 liters of
water, as all the water rejected in the process will be reused for new distillations. The results
demonstrated that, due to the significant savings generated by the proposed system
compared to the current model, the project can be implemented and replicated in other
university laboratories. The findings also highlighted that this water reuse system is an
excellent sustainable alternative for managing water resources.
Resumo: A água é um recurso natural indispensável para a vida no planeta Terra. Possui um enorme
valor ambiental, social e econômico, fundamental para a sobrevivência do ser humano e dos
ecossistemas no nosso planeta. A boa gestão dos recursos hídricos de uma sociedade deve
considerar o reuso, pois assim além de gerar economia, evita a escassez hídrica. No Brasil, a
água é utilizada principalmente para irrigação de lavouras, abastecimento público, atividades
industriais, geração de energia, extração mineral, aquicultura, navegação, turismo e lazer. O
presente trabalho leva em conta o problema de desperdício de recurso hídrico no processo
de destilação da água, esse trabalho se dedica a criar um sistema para reutilização da água
de rejeito gerada durante o processo, a fim de, gerar economia e evitar o desperdício.
Fazendo um comparativo entre os dois métodos de produção da água destilada (modo usual
versus modo proposto), podemos notar que, enquanto o modo de produção usual utiliza-se
cerca de 8580 (destilada + rejeito) litros de água ao longo de 12 meses, o modo de produção
proposto nesse trabalho utiliza apenas 627 litros de água já que toda água rejeitada no
processo será reaproveitada para novas destilações. Os resultados obtidos nesse trabalho
mostraram que devido a grande economia gerada pelo sistema proposto no projeto e em
comparação com o modelo atual, o projeto se mostra viável e com possibilidade de ser
replicado para os outros laboratórios da universidade. Tais resultados também evidenciaram
que esse sistema de reutilização da água é uma ótima alternativa sustentável do uso dos
recursos hídricos.2025-01-30T00:00:00ZEstudo da resistência à corrosão do revestimento a base da liga Zn-Ni obtido por eletrodeposição em aço SAE 1020Gomes, Anyelle Maria Torreshttps://repository.ufrpe.br/handle/123456789/66682025-01-27T20:12:40Z2023-09-18T00:00:00ZTítulo: Estudo da resistência à corrosão do revestimento a base da liga Zn-Ni obtido por eletrodeposição em aço SAE 1020
Autor: Gomes, Anyelle Maria Torres
Abstract: Concern for the environment and environmental laws increasingly increase the desire to
reduce waste disposal costs, with this in mind, a good alternative is the use of metal
biodigesters. However, the organic material and the product of the biochemical process
reduce the useful life of this equipment. Aiming for good durability and efficiency of this
equipment, studies have been carried out to apply coatings with materials that are highly
resistant to corrosion through the electrodeposition process. The objective of this study
was to evaluate the corrosion resistance of coatings based on the Zn-Ni alloy obtained by
electrodeposition on SAE 1020 steel sheet. The process parameters, bath temperature and
current density used to obtain coatings with the alloy Zn-Ni were optimized using
factorial experimental design and the results analyzed by the Response Surface
Methodology (MSR). The Ni-Zn alloy coatings were characterized using X-ray
diffraction (XRD), scanning electron microscopy (SEM) and electrochemical corrosion
measurements by Linear Potentiodynamic Polarization (PPL) and Electrochemical
Impedance Spectrometry (EIE). The coating with the alloy Zn68.9Ni31.1 at.%, deposited
with current density 25 A/cm2 and bath temperature 60oC, presented the best results
against corrosion, as it presented the lowest values of corrosion current, thus indicating a
less dissolution of the coating.
Resumo: A preocupação com o meio ambiente e as leis ambientais aumentam cada vez mais a
necessidade de diminuir os custos com o descarte de resíduos, pensando nisso uma boa
alternativa é o uso de biodigestores metálicos. Entretanto, o material orgânico e o produto
do processo bioquímico promovem a redução da vida útil desse equipamento. Visando
uma boa durabilidade e eficiência desse equipamento, estudos vêm sendo realizados para
aplicação de revestimentos com materiais de alta resistência a corrosão por processo de
eletrodeposição. Objetivou-se neste estudo avaliar a resistência a corrosão dos
revestimentos a base da liga de Zn-Ni obtida por eletrodeposição sobre chapa do aço SAE
1020. Os parâmetros de processo, temperatura do banho e densidade da corrente usados
para obtenção dos revestimentos com a liga Zn-Ni foram otimizados utilizando o
planejamento experimental fatorial e os resultados analisados pela Metodologia de
Superfície de Resposta (MSR). Os revestimentos da liga de Ni-Zn foram caracterizados
usando difração de raios X (DRX), microscopia eletrônica de varredura (MEV) e medidas
eletroquímicas de corrosão por Polarização Potenciodinâmica Linear (PPL) e
Espectrometria de Impedância Eletroquímica (EIE). O revestimento com a liga
Zn68,9Ni31,1 at.%, depositado com densidade de corrente 25 A/cm2 e temperatura do
banho 60oC, apresentou os melhores resultados frente a corrosão, pois apresentou os
menores valores de corrente de corrosão, indicando assim uma menor dissolução do
revestimento.2023-09-18T00:00:00ZGesso de revestimento destinado à construção civil reforçado com nanopartículas de óxido de grafeno: análise da resistência mecânicaFirmino, Daniel Ardileshttps://repository.ufrpe.br/handle/123456789/66672025-01-27T20:09:45Z2024-03-01T00:00:00ZTítulo: Gesso de revestimento destinado à construção civil reforçado com nanopartículas de óxido de grafeno: análise da resistência mecânica
Autor: Firmino, Daniel Ardiles
Abstract: Plaster is a widely used material in civil construction, employed for both structures and
general coatings. Graphene Oxide, known for reinforcing structures and being utilized
as a reinforcement in civil engineering, is expected to provide additional strength to the
structure when incorporated into plaster. This study focused on reinforcing plaster
coating with graphene oxide at a concentration of 0.01% by mass, aiming to optimize
mass and examine its mechanical properties. A comparison was made between
samples with and without oxide addition. The graphene oxide was obtained through
the modified Hummers method. Two characterization techniques, X-ray Diffraction
(XRD) and Scanning Electron Microscopy (SEM), were employed for morphological
and structural analysis. Sample preparation adhered to parameters outlined in the NBR
12128 (ABNT, 2019) and NBR 12129 (ABNT, 2017) standards. The results revealed
that plaster with added graphene oxide exhibited a reduction of over half in
compressive strength compared to plaster without the additional load. SEM images
highlighted the accumulation of graphene oxide in specific regions of the plaster,
potentially contributing to this decrease in strength.
Resumo: O gesso é um material amplamente utilizado na construção civil, tanto para estruturas
quanto para revestimentos em geral. O óxido de grafeno (OG), muito utilizado como
reforço em diversas áreas da engenharia civil, pode proporcionar um reforço adicional
à estrutura do gesso quando incorporado a ele. Este estudo abordou o reforço do
gesso de revestimento com óxido de grafeno em concentração de 0,01% em massa,
com o objetivo de otimizar a massa e verificar suas propriedades mecânicas. Foi
realizado um estudo comparativo entre amostras com adição de óxido e sem adição.
O óxido de grafeno foi obtido pelo método de Hummers modificado. Para a análise
morfológica e estrutural, foram empregadas duas técnicas de caracterização: Difração
de Raio-X (DRX) e Microscopia Eletrônica de Varredura (MEV). A preparação das
amostras seguiu parâmetros de acordo com as normas NBR 12128 (ABNT, 2019) e
NBR 12129 (ABNT, 2017). Os resultados revelaram que o gesso com adição de óxido
de grafeno apresentou uma redução de mais da metade em relação à resistência à
compressão quando comparado ao gesso sem a carga adicional. Medições
mostraram uma densidade aparente muito menor do gesso reforçado, fator que
somado a uma possível falta de interação na interface gesso/OG, podem ter
contribuído para a diminuição dessa resistência mecânica.2024-03-01T00:00:00Z